Polyurethane resin-based binder, for creating decorative surfaces with rubber and aggregate chippings.
FOR APPLYING IN-SITU:
LARGE-SCALE APPLICATIONS:
For any sprayed applications please consult our technical department.
In opaque plastic container with net weight of 25 kg.
Store in the original unsealed packaging without between a temperature of 15 - 25ºC in a dry, well-ventilated place. The product has a useful life of 6 months.
The dosage must be previously checked as the porosity or type of aggregate or mineral could require varying percentages. The following table shows the approximate % for creating decorative surfaces (for guidance purposes only).
DOSAGE | TYPES |
3.5 - 4% | For non-porous stones of a diameter of 50 mm or above |
4 - 4.5% | For non-porous stones of a diameter between 5 and 50 mm |
> 4.5% | For non-porous stones of a diameter less than 5 mm |
13% | For rubber chips pavements applied in situ (base coat) |
15% | For rubber chips pavements applied in situ (finish coat) |
Appearance: | Translucent |
Density at 25ºC: | 1.061 ± 0.020 g/cm3 |
Viscosity at 25ºC: | 4400 ± 200 cps |
Contents in solid particles: | 100% |
Flash point: | > 200ºC |
% NCO: | 9.65 ± 0.20 % |
FINISHED PRODUCT CHARACTERISTICS
TEST | STANDARD | RESULT |
Stretch to break point (%) | UNE 53510 | - |
Tensile strength (MPa) | UNE 53510 | - |
Tear strength (N/mm) | UNE 53510 | - |
Hardness (Shore A %) | UNE 53130 | - |
Density (g/cm3) | UNE 53526 | - |
Abrasion (mm3) | UNE 53527 | - |
Time between coats | 12 hours |
Start-up time 23ºC | 48 hours |
Fully cured at 23 ºC | 96 hours |
Complete curing (industrial application) 160ºC | 12 minutes |