Resina Inyección Epoxi BV
Additional information
Product
5 kilos kits. Store the product in dry and fresh places inside their closed original container at temperatures between +5ºC and +30ºC. Due date: 12 months from manufacturing date.Features and applications
- To fill and seal the cracks in concrete structures such as bridges, industrial flooring, docks, beams, pillars or walls.
- Monolithic reparation of reinforced concrete and mass concrete.
- Great penetration due to its low viscosity.
- Great adherence to concrete, mortars, steal, and natural and artificial stones.
- No reaction against polymerization Structural union between concretes with cracks.
- Interior and exterior application.
- Vertical and horizontal application.
- Do not apply in cracks with movements. Compatible with humid substrates.
- Excellent mechanical resistance.
Substrates
Surface must be clean and dry, free of dust, grease, oils or spare particles. It is important to clean the cracks with compressed air to remove dust and dirt. When dealing with very porous substrates, add a 5 - 10 % extra resin from the amounts given in the data sheet. Minimum temperature of the substrate + 5º C and maximum temperature + 30º C.
Instructions for use
- Mix component A with a low-speed mechanical mixer (< 600 r/min) then add component B to component A and continue mixing for 3-4 minutes until obtaining a homogeneous mixture.
- In horizontal fissures it can be poured by gravity until saturation.
- Product in vertical cracks is injected in the usual way by means of a manual or mechanical pump or injection pot.
- Use an injecting tool for vertical cracks.
- The intersection of the crack must be ensured when placing the injectors, since the cracks do not always follow a straight line.
- Each injector is placed every 20 - 30 cm.
- Superficially seal the fissure with Morcemrest Epoxy T or Morcem Rapid Ultra, in order to prevent resin leaks during application.
- Cracks should be refilled from bottom to top. After the injection process, of 24 hours later, remove the injectors and the sealing material and carry out the finishing work.
Cautions and recommendations
- Please consult our Technical Department in case of any specific application which may not be specified in this Technical Data Sheet.
- In order to clean the tools, it is advisable to use solvents before the products gets hard.
- Once the product gets hard, it will only be removed by mechanical means.
- For all information required regarding safety in handling, transportation, storage and use of the product, consult the label and the updated version of the Product Safety Sheet.
Technical data
| Property | Value |
| Colour | Colourless |
| Specific weight of component A | 1.12 gr/cm3 |
| Specific weight of component B | 0.95 gr/cm3 |
| Specific weight of component A + B | 1.10 gr/cm3 |
| Solid content | >99 |
| Mixture ratio | A/B = 6.7/3.3 |
| Post Life 20º C | 30-40 minutes (*) |
| Viscosity A + B | 50N/mm2 |
| Resistance to traction | 51 N/mm2 |
| Resistance to bending | 70 Mpa |
| Date | 60 mm |
| Module E | 3020 Mpa |
| Elongation at break | 5% |
| Consumption | Depending on creacks and substrate´s porosity |
(*) Post-life is subject to the conditions of the environment where it is applied. Temperatures and humidity may affect the polymeration timings.